Semicrystalline Polyesters Based on a Novel Renewable Building Block

Research output: Contribution to journalArticleAcademicpeer-review

63 Citations (Scopus)

Abstract

Isohexides, like e.g. isosorbide, are well-known carbohydrate-based rigid diols which are capable of dramatically increasing the glass transition temperature of polyesters. However, their relatively low reactivity has thus far hampered large-scale industrial applications in the polymer field. Recently, with the aim to increase reactivity while at the same time retain rigidity, we have developed a new isoidide dicarboxylic acid (IIDCA) by transforming the secondary hydroxyls into carboxylate functionalities. Here we report the first polymers based on IIDCA and linear a,¿-diols. The novel polyesters were obtained via melt polymerization and exhibited weight-average molecular weights in the range of 13¿000–34¿000 g/mol and polydispersities close to 2.0. NMR analyses showed that the exo–exo configuration of the isoidide dicarboxylate units was preserved during synthesis. Both differential scanning calorimetry and wide-angle X-ray diffraction analyses showed that the IIDCA polyesters are semicrystalline materials. A systematic study on structure–thermal properties relations among relevant series of polyesters, such as isomeric polymers based on isoidide, revealed several interesting differences in melting and glass transition temperatures, which are thought to be related to variations in chain packing and free volume.
Original languageDutch
Pages (from-to)5069-5080
JournalMacromolecules
Volume45
Issue number12
DOIs
Publication statusPublished - 2012

Keywords

  • succinic acid
  • poly(butylene terephthalate)
  • coating applications
  • melting behavior
  • polymers
  • resources
  • isosorbide
  • chemistry
  • 1,4/3,6-dianhydrohexitols
  • crystallization