TY - JOUR
T1 - Micrometric pyrite catalyzes abiotic sulfidogenesis from elemental sulfur and hydrogen
AU - van der Graaf, Charlotte M.
AU - Sánchez-España, Javier
AU - Ilin, Andrey M.
AU - Yusta, Iñaki
AU - Stams, Alfons J.M.
AU - Sánchez-Andrea, Irene
PY - 2024/7/31
Y1 - 2024/7/31
N2 - Hydrogen sulfide (H2S) in environments with temperatures below 100 °C is generally assumed to be of microbial origin, while abiotic H2S production is typically restricted to higher temperatures (T). In this study, we report an abiotic process for sulfidogenesis through the reduction of elemental sulfur (S0) by hydrogen (H2), mediated by pyrite (FeS2). The process was investigated in detail at pH 4 and 80 °C, but experimental conditions ranged between 40 and 80 °C and pH 4–6. The experiments were conducted with H2 as reducing molecule, and µm-sized spherical (but not framboidal) pyrite particles that formed in situ from the H2S, S0 and Fe2+ present in the experiments. Fe monosulfides, likely mackinawite, were identified as potential pyrite precursors. The absence of H2 production in controls, combined with geochemical modelling, suggests that pyrite formation occurred through the polysulfide pathway, which is unexpected under acidic conditions. Most spherical aggregates of authigenic pyrite were composed of nanometric, acicular crystals oriented in diverse directions, displaying varying degrees of organization. Although it was initially hypothesized that the catalytic properties were related to the surface structure, commercially sourced, milled pyrite particles (< 50 μm) mediated H2S production at comparable rates. This suggests that the catalytic properties of pyrite depend on particle size rather than surface structure, requiring pyrite surfaces to act as electron shuttles between S0 and H2.
AB - Hydrogen sulfide (H2S) in environments with temperatures below 100 °C is generally assumed to be of microbial origin, while abiotic H2S production is typically restricted to higher temperatures (T). In this study, we report an abiotic process for sulfidogenesis through the reduction of elemental sulfur (S0) by hydrogen (H2), mediated by pyrite (FeS2). The process was investigated in detail at pH 4 and 80 °C, but experimental conditions ranged between 40 and 80 °C and pH 4–6. The experiments were conducted with H2 as reducing molecule, and µm-sized spherical (but not framboidal) pyrite particles that formed in situ from the H2S, S0 and Fe2+ present in the experiments. Fe monosulfides, likely mackinawite, were identified as potential pyrite precursors. The absence of H2 production in controls, combined with geochemical modelling, suggests that pyrite formation occurred through the polysulfide pathway, which is unexpected under acidic conditions. Most spherical aggregates of authigenic pyrite were composed of nanometric, acicular crystals oriented in diverse directions, displaying varying degrees of organization. Although it was initially hypothesized that the catalytic properties were related to the surface structure, commercially sourced, milled pyrite particles (< 50 μm) mediated H2S production at comparable rates. This suggests that the catalytic properties of pyrite depend on particle size rather than surface structure, requiring pyrite surfaces to act as electron shuttles between S0 and H2.
U2 - 10.1038/s41598-024-66006-z
DO - 10.1038/s41598-024-66006-z
M3 - Article
C2 - 39085257
AN - SCOPUS:85200253799
SN - 2045-2322
VL - 14
JO - Scientific Reports
JF - Scientific Reports
M1 - 17702
ER -