How Particle Deformability Influences the Surfactant Distribution in Colloidal Polymer Films

The distribution of surfactants in waterborne colloidal polymer films is of significant interest for scientific understanding and defining surface properties in applications including pressure-sensitive adhesives and coatings. Because of negative effects on appearance, wetting, and adhesion, it is desirable to prevent surfactant accumulation at film surfaces. The effect of particle deformation on surfactant migration during film formation was previously investigated by Gromer et al. through simulations, but experimental investigations are lacking. Here, we study deuterium-labeled sodium dodecyl sulfate surfactant in a poly(butyl acrylate) latex model system. The particle deformability was varied via cross-linking of the intraparticle polymer chains by differing extents. The cross-linker concentration varied from 0 to 35 mol % in the copolymer, leading to a transition from viscoelastic to elastic. Ion beam analysis was used to probe the dry films and provide information on the near-surface depth distribution of surfactant. Films of nondeformable particles, containing the highest concentration of cross-linker, show no surfactant accumulation at the top surface. Films from particles partially deformed by capillary action show a distinct surfactant surface layer (ca. 150 nm thick). Films of coalesced particles, containing little or no cross-linker, show a very small amount of surfactant on the surface (ca. 20 nm thick). The observed results are explained by considering the effect of cross-linking on rubber elasticity and applying the viscous particle deformation model by Gromer et al. to elastically deformed particles. We find that partially deformed particles allow surfactant transport to the surface during film formation, whereas there is far less transport when skin formation acts as a barrier. With elastic particles, the surfactant is carried in the water phase as it falls beneath the surface of packed particles. The ability to exert control over surfactant distribution in waterborne colloidal films will aid in the design of new high-performance adhesives and coatings.